Abstract
This paper highlights a methodology for failure analysis of cast grinding ring of a ball and race mill. It investigates the root cause of premature failure of cast grinding ring. The grinding ring was made of Ni Hard IV. Grinding ring of ball and race mill failed after giving the life only 2861 running hours. It was premature failure against the required useful life of 6500 running hours. The process of critical investigation of failure analysis includes visual observation, chemical analysis, microstructure analysis, and evaluation of hardness, analysis of erection process and operational analysis. The cast ring was failed with the indication of direct separation of surface from the outer periphery of ring. No evidence of faulty chemical composition, microstructure and erection procedure were observed. Hardness was found around 400 BHN and inadequate spring pressure on ring was also observed during operation of ball and race mill which had caused the radial movement of the ball in ball track of the lower ring, resulting radial thrust on the collar of the ring and it failed from that area.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Similar content being viewed by others
References
Dennies, D.P.: How to Organize a Failure Investigation. ASM International, Ohio (2005)
Wulpi, D.J.: Techniques of failure analysis. In: Miller, B. (ed.) Understanding How Components Fail. ASM International, Ohio (2000)
Brooks, C.R., Choudhury, A.: Metallurgical Failure Analysis. McGraw-Hill, New York (1993)
Graham, R.: Strategies for failure analysis. ASM Adv. Mater. Process. 172(11), 45–50 (2004)
Ryder, D.A., Davies, T.J., Brough, I., Hutchings, F.R.: General practice in failure analysis. Failure analysis and prevention. Metals handbook, American Society for Metal, Ohio (1986)
Vander Voort, G.F.: Conducting the Failure Examination Practice. ASM Handbook. ASM International, Ohio (2002)
German, V., et al.: Conical diamond element bit sets new performance benchmarks drilling extremely hard carbonate/chert formations. In: Perm Region Russia SPE/IADC Drilling Conference and Exhibition, pp. 1905–1920 (2015)
Xu, Z., et al.: Hybrid drill bit combining fixed-cutter and roller-cone elements exceeds expectations in challenging application in Tarim Basin China. In: IADC/SPE Asia Pacific Drilling Technology Conference, Thailand, pp. 348–354 (2014)
Al-Enezi, D., et al.: Focused engineering initiative produces new 16-in roller cone TCI design to solve carbonate. In: Drilling challenges in Northern Kuwait 19th SPE Middle East Oil and Gas Show and Conference, Bahrain, pp. 441–449 (2015)
Gupta, G.K., Chattopadhyaya, S.: Critical failure analysis of superheater tubes of coal based boiler. Strojniški vestnik - J. Mech. Eng. 63(5), 287–299 (2017)
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 Springer Nature Switzerland AG
About this paper
Cite this paper
Guptaa, G.K., Chattopadhyayab, S. (2019). Critical Failure Analysis of Lower Grinding Ring of Ball and Race Mill. In: Hloch, S., Klichová, D., Krolczyk, G., Chattopadhyaya, S., Ruppenthalová, L. (eds) Advances in Manufacturing Engineering and Materials. Lecture Notes in Mechanical Engineering. Springer, Cham. https://doi.org/10.1007/978-3-319-99353-9_27
Download citation
DOI: https://doi.org/10.1007/978-3-319-99353-9_27
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-99352-2
Online ISBN: 978-3-319-99353-9
eBook Packages: EngineeringEngineering (R0)